Profile:
Our company( Wugang Chang Yu Long Industry and Trade Co.,Ltd. ) special in Steel Product, Steel Plate, carbon steel plate, hot rolled steel plate, cold rolled steel plate, stainless steel plates, steel circle, color coated steel plate, hot plate, steel coils, etc.
Carbon steel plate S10C-S55C Steel Plate
Characteristics and Scope of Application:
S10C has low mechanical strength, good plasticity and toughness, is easy to mold in cold state, is easy to cut, has good welding performance, and can be used to improve surface hardness
Carbonization and cyanide treatment. S10C is used to manufacture low strength welded parts, cold stamped parts, forgings, and carburized parts such as bolts, washers, partitions, shells, etc.
Chemical composition:
Carbon C: 0.08~0.13
Silicon Si: 0.15~0.35
Manganese Mn: 0.30-0.60
Sulfur S: ≤ zero point zero three zero
Phosphorus P: ≤ zero point zero three zero
Chromium Cr: ≤ zero point two zero
Nickel Ni: ≤ zero point two five
Copper Cu: ≤ zero point two five
Mechanical properties:
Tensile strength σ b (MPa): ≥ 335 (34)
Yield strength σ s (MPa): ≥ 205 (21)
Elongation rate δ 5 (%): ≥ 31
Shrinkage rate of cross-section (%): ≥ 55
Hardness: Untreated, ≤ 137HB
Sample size: The sample size is 25mm
Heat treatment specifications and metallographic structure:
Heat treatment specification: normalizing, 930 ºC.
Metallographic structure: ferrite+pearlite.
Delivery status: Delivered in a non heat treated or heat treated (annealed, normalized, or high-temperature tempered) state. Delivery in heat treated condition should be specified in the contract
Those not specified shall be delivered without heat treatment.
S10C low carbon steel has the following main performance characteristics:
1. Excellent weldability: Under conventional welding methods such as arc welding and gas shielded welding, good welding joints can be obtained while maintaining strength and toughness.
2. Good malleability and machinability: S10C low carbon steel has high plasticity and variability, and can be formed through forging, cold and hot processing, and other methods
Suitable for processing and manufacturing various mechanical components.
3. Moderate strength and toughness: S10C low carbon steel has moderate strength, higher hardness and elastic modulus compared to other common low carbon steels
Can meet the usage requirements of most structural components.
4. Good toughness and impact resistance: Even in low temperature environments, S10C low carbon steel still maintains good toughness and impact resistance, thus requiring cold resistance
Widely applicable in various occasions.
The main applications of S10C low carbon steel include but are not limited to the following aspects:
1. Manufacturing of mechanical components: Due to its excellent machinability and malleability, it is widely used in the manufacturing of various mechanical components, including gears, shafts, and rolling mills
Rollers, pins, etc.
2. Manufacturing of structural components: S10C low carbon steel can be used to manufacture structural components such as bridges, building structures, and supports, with good strength and durability.
3. Automotive manufacturing: S10C low-carbon steel can be used to manufacture the chassis, frame, and body components of automobiles, with high comfort and safety performance.
4. Shipbuilding: Due to its excellent weldability and corrosion resistance, S10C low-carbon steel is widely used in the field of shipbuilding, including ship structure and propulsion
Equipment, etc.
Applications: Various types of steel components for riveting, bolting, welding.
Quick Details:
Standard: GB3274, GB711, JIS G 3101, JIS G 3106, JIS G 4051, DIN17100, ASTM, BS4360, EN10025, EN10083-2, ISO630
Grade: S10C-S55C
Place of Origin: Henan China (Mainland)
Brand Name: Wu Gang Hong Xing
Type: Steel plate Surface treatment: Hot rolled
Packaging & Delivery:
Packaging detail: Bundle, loose and bare or according customer inquire
Delivery detail: Depend on the customer inquire
Specifications:
Steel Plate S10C-S55C
1 Grade: S10C-S55C
2 T: 6-700mm; Length: 3000-12000mm; W: 1500-4000mm;
3 Delivery time: Average Period in 30 days.
| components |
C
|
Si
|
Mn
|
P
≤ |
S
≤ |
N |
TAl |
V |
Nb |
Ni |
| 0.06-012 |
0.15-0.30 |
0.25-0.50 |
0.030 |
0.030 |
|
|
|
|
|
| Use |
Various types of steel components for riveting, bolting, welding. |
| size |
3000-118800mm*1500-4000mm*6-700mm |
| Thickness |
6-700mm |
| Standard |
GB700 |
| Material |
S10C-S55C |
| Packing |
According to the demand of the customer inquire |
| Surface treatment |
Hot-rolled |
| Delivery time |
According to the quantity; asap, average period in 30 days. |