| Customization: | Available |
|---|---|
| Type: | Stainless Steel Sheets |
| Standard: | ASTM, AISI, GB, JIS, DIN, EN |
|
Still deciding? Get samples of US$ 0/Piece
Request Sample
|
Suppliers with verified business licenses
Audited Supplier Audited by an independent third-party inspection agency
| PRODUCT NAME | high tensile 904l No.1finish stainless steel plates | |
| GRADE | 201 / 202 / 301 / 302 / 304 / 304L / 305 / 309 / 310s / 316 / 316L 409 / 409L / 410 / 410L / 430 /904L |
|
| SURFACE FINISH | NO.1 | |
| SURFACE PROTECTION | Paper Or PVC | |
| MATERIAL STANDARDS | ASTM /BV /AISI/GB /EN /JIS | |
| HOT ROLLED | Width | 1000~2000mm |
| Length | 2000~6000mm | |
| Thickness | 3.00~60mm | |
| Normal Size | 1500*6000/ 1800*6000/2000*6000mm | |
| Finish | No.1 | |
| BRAND | TISCO,JISCO,LISCO,BAO STEEL | |
| MEASURING WEIGHT | By Theory Or Actual Weight | |
| APPLICATION | Construction,Petroleum&Chemical,Electricity,Food processing,Medical,Machinery,Hardware etc | |
| FINISH | DEFINITION | APPLICATION |
| BA | By heat treatment after cold rolling. | Kitchen utensils, Electric equipment, Building construction. |
| 2B | Cold rolling, then heat treatment,lastly by cold rolling | Medical equipment, Food industry, Construction material, Kitchen utensils. |
| HL | Hair Line | Building Construction. |
| NO.1 | By heat treatment,then pickling or processes corresponding. | Chemical tank, pipe. |
| NO.4 | By polishing with No.150 to No.180 abrasives specified in JIS R6001. | Kitchen utensils, Building construction, Medical equipment. |
| NO.3 | By polishing with No.100 to No.120 abrasives specified in JIS R6001. | Kitchen utensils, Building construction. |
| STEEL GRADE | DENSITY(g/cm3) |
| 304 / 304L / 305 / 321 | 7.93 |
| 201 / 202 / 301 / 302 | |
| 316 / 316L / 347 | 7.98 |
| 309S / 310S | |
| 405 / 410 / 420 | 7.75 |
| 409 / 430 / 434 | 7.7 |
| 904L | 8 |
| Grade | C (Max) |
Mn (Max) |
P (Max) |
S (Max) |
Si (Max) |
Cr (Max) |
Ni (Max) |
Mo (Max) |
Cu/Other (Max) |
| 201 | 0.15 | 5.50~7.50 | 0.060 | 0.03 | 1.00 | 16.00~18.00 | 1.0~3.50 | - | - |
| 202 | 0.15 | 7.5~10.00 | 0.060 | 0.03 | 1.00 | 17.00- | 4.0~6.0 | ||
| 301 | 0.15 | 2.00 | 2.00 | 0.03 | 1.00 | 16.00~18 | 6.00~8.00 | ||
| 304 | 0.08 | 2.00 | 0.045 | 0.03 | 1.00 | 18.00~20.00 | 8.00~10.00 | - | - |
| 304L | 0.03 | 2.00 | 0.045 | 003 | 1.00 | 18.00~20.00 | 8.00~11.00 | - | - |
| 310S | 0.08 | 2.00 | 0.045 | 0.03 | 1.5 | 24.00~26.00 | 19.00~22.00 | - | - |
| 316L | 0.03 | 2.00 | 0.045 | 0.03 | 1.00 | 16.00~18.00 | 10.00~14.00 | 2.00~3.00 | - |
| 317 | 0.08 | 2.00 | 0.045 | 0.03 | 0.75 | 18.00~20.00 | 11.00~14.00 | 3.00~4.00 | - |
| 409 | 0.08 | 1.00 | 0.045 | 0.03 | 1.00 | 10.5~11.75 | 0.50 | - | - |
| 409L | 0.03 | 1.00 | 0.04 | 0.02 | 1.00 | 10.5~11.7 | - | - | - |
| 410 | 0.15 | 1.00 | 0.035 | 0.03 | 0.50 | 11.5~13.00 | - | - | - |
| 410L | 0.03 | 1.00 | 0.035 | 0.03 | 1.00 | 11.00~13.00 | - | - | - |
| 904L | 0.020 | 2.0 | 0.045 | 0.035 | 0.45 | 19~23 | 23~28 | 4.0~5.0 | 1.0~2.0 |
| Mechanical Properties | Value |
| Tensile Strength σb (MPa) | ≥ 520 |
| Conditions Yield Strength σ0.2 (MPa) | ≥ 205 |
| Elongation δ5 (%) | ≥ 40 |
| Section Shrinkage ψ(%) | ≥ 60 |
| Hardness | ≤ 187HB ;≤ 90HRB ; ≤ 200 HV |